Properties
- Mechanical Properties
Value Units Test Method / Conditions Stress at Break (Stressb) (Dry) 138 MPa ISO 527-1/-2 Strain at Break (Strain b) (Dry) 3.6 % ISO 527-1/-2 - Thermal Properties
Value Units Test Method / Conditions Coefficient of Linear Thermal Expansion(Normal) (at 23°C - 55°C) 116.00×10⁻⁶ - 116.00×10⁻⁶ /K ISO 11359-1/-2 HDT B (0.45 MPa) 220 °C ISO 75-1/-2 HDT A (1.80 MPa) 200 °C ISO 75-1/-2 Melting Temperature(10°C/min) 220 °C ISO 11357-1/-3 /DSC Thickness Tested (b1) 0.73 mm IEC 60695-11-10 Coefficient of Linear Thermal Expansion (Parallel) (at 23°C - 55°C) 21.00×10⁻⁶- 21.00×10⁻⁶ /K ISO 11359-1/-2 - Material Specific Properties
Value Units Test Method / Conditions Viscosity Number 160 cm³/g ISO 307, 1157, 1628 - Rheological Calculation Properties
Value Units Test Method / Conditions Melt Volume-Flow Rate 20 cm³/10min ISO 1133 Molding Shrinkage (Normal) 0.7 % ISO 294-4 Molding Shrinkage (Parallel) 0.3 % ISO 294-4 - Other Properties
Value Units Test Method / Conditions Water Absorption (Equilibrium in Water, at 23°C) 5.90 - 6.50 % Similar to ISO 110 Moisture Absorption, Equilibrium (at 23°C/50% r.h) 1.80 - 2.20 % Similar to ISO 111