Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color (Properties)
- Mechanical Properties
Value Units Test Method / Conditions Molding Shrinkage(Constrained)³ 0.25 % Tensile Modulus (Cond.) 5600 MPa ISO 527-1/-2 Tensile Modulus (Dry) 9600 MPa ISO 527-1/-2 Stress at Break (Dry) 180 MPa ISO 527-1/-2 Stress at Break (Cond.) 90 MPa ISO 527-1/-2 Strain at Break (Dry) 3 % ISO 527-1/-2 Strain at Break (Cond.) 6 % ISO 527-1/-2 Charpy Unnotched Impact Strength (23°C) (Dry) 80 kJ/m² ISO 179/1eU Flexural Modulus (Cond.) 5000 MPa ISO 178 Charpy Unnotched Impact Strength (23°C) (Cond.) 80 kJ/m² ISO 179/1eU Flexural Modulus (Dry) 8300.0 MPa ISO 178 Flexural Strength (Cond.) 150 MPa ISO 178 Flexural Strength (Dry) 250.0 MPa ISO 178 Charpy Notched Impact Strength (23°C) (Cond.) 20 kJ/m² ISO 179/1eA Charpy Unnotched Impact Strength (at -30°C) (Dry) 65.0 kJ/m² ISO 179/1eU Charpy Notched Impact Strength (23°C) (Dry) 12 kJ/m² ISO 179/1eA Charpy Notched Impact Strength (Dry) (at -30°C) 9 kJ/m² ISO 179/1eA Izod Notched Impact Strength (Dry) (at 23°C) 12 kJ/m² ISO 180/A - Typical Properties
Value Units Test Method / Conditions Polymer Abbreviation (at 23°C) PA6-GF30 - - Density (at 23°C) 1360 kg/m³ ISO 1183 Viscosity Number (0.5% in 96% H₂SO₄) (at 23°C) 142 cm³/g ISO 307, 1157, 1628 Water Absorption (Equilibrium in Water, at 23°C) 6.3 - 6.9 % Similar to ISO 94 Moisture Absorption, Equilibrium (at 23°C/50% r.h) 1.9 - 2.3 % Similar to ISO 95 Bulk Density 0.7 g/cm³ - - Thermal Properties
Value Units Test Method / Conditions Deflection Temperature Under Load 1.8 Mpa (HDT A) 205.0 °C ISO 75-1/-2 Deflection Temperature Under Load 0.45 MPa (HDT B) 218.0 °C ISO 75-1/-2 Service Temperature (Short Cycle Operation) max. 200 °C - Coefficient of Linear Thermal Expansion, Longitudinal (at 23°C - 55°C) 18.4×10⁻⁶ /K ISO 11359-1/-2 Coefficient of Linear Thermal Expansion, Transverse (at 23°C - 55°C) 96.4×10⁻⁶ /K ISO 11359-1/-2 - Electrical Properties
Value Units Test Method / Conditions Electric Strength K20/K20, (60*60*1 mm³) (Cond.) (at 23°C - 55°C) 31 kV/mm IEC 60243-1 Electric Strength K20/K20, (60*60*1 mm³) (Dry) (at 23°C - 55°C) 40 kV/mm IEC 60243-1 - Shrinkage
Value Units Test Method / Conditions Processing Shrinkage, Constrained, Longitudinal (Tm = 280°C, Tw = 80°C) ⁴ 0.25 % - - Flammability
Value Units Test Method / Conditions Ul94 Flammability Rating (at Nominal 1.5mm) HB class (mm) IEC 60695-11-10 Automotive Materials (Thickness > 1mm) ⁴ Passed - ISO 3795, FMVSS 302 - Injection Molding
Value Units Test Method / Conditions Melt Temperature (Range) 270 - 290 °C Mold Temperature (Range) 80 - 90 °C - Residence Time max. 10 min - - Drying
Value Units Test Method / Conditions Moisture Content (Recommended) (at 23°C - 55°C) ¹ 0.03 - 0.06 % - Dryer Temperature ² 80 °C - Drying Time ³ 4 h - Moisture Content max. 0.21 % - - Machine Settings
Value Units Test Method / Conditions Temperature Hopper Throat 80 °C - Cylinder Temperature 1 (Feed Zone) 260 °C - Cylinder Temperature 2 (Compression) 270 °C - Cylinder Temperature 3 (Metering - Zone, in Front of The Screw) 280 °C - Cylinder Temperature 4 (Nozzle) 280 °C - Peripheral Screw Speed max. 0.3 m/s - Processing Properties
Value Units Test Method / Conditions Melting Temperature 220.0 °C ISO 11357-1/-3/DSC Melt Temperature (Injection Molding/Extrusion) 270 - 290 °C - Mold Temperature (Injection Molding) 80 - 90 °C - Pre/Post - Processing, Pre - Drying, Time 4 h - - Note
- If product name or properties don't state otherwise.
- The asterisk symbol '*' signifies inapplicable properties.
- Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 280°C, TW = 80°C
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
Safety & Health
- Product Safety
In case processing is done under conditions as recommended (cf. processing data sheet) melts are thermally stable and do not generate hazards by molecular degradation or the evolution of gases and vapors.
Like all thermoplastic polymers the product decomposes on exposure to excessive thermal load, e.g. when it is overheated or as a result of cleaning by burning off.
Packaging & Availability
- Packaging Information
Standard packs are bag and bulk container (octagonal IBC=intermediate bulk container made from corrugated board with a liner bag).
Other packaging materials and shipping in road or rail silo wagons are possible by agreement.
Storage & Handling
- Storage Information
The containers should only be opened immediately before processing or drying.
To ensure that the delivered product absorbs as little moisture as possible, the containers should be stored in dry rooms and always carefully closed again after partial quantities have been withdrawn.
In principle, the product can be stored for a long period of time.
Containers stored in cold rooms should be equalized to ambient temperature before opening in order to avoid condensation on the granules.
Regardless of the storage conditions, the product should be pre-dried according to our recommendations and the machine should preferably be loaded using a closed conveyor system.