Properties
- Color (Properties)
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Modulus (Cond.) 1000 MPa ISO 527-1/-2 Tensile Modulus (Dry) 3100 MPa ISO 527-1/-2 Yield Stress (50 mm/min) (Cond.) 40 MPa ISO 527-1/-2 Yield Stress (50 mm/min) (Dry) 85 MPa ISO 527-1/-2 Yield Strain (50 mm/min) (Cond.) 20 % ISO 527-1/-2 Yield Strain (50 mm/min) (Dry) 4 % ISO 527-1/-2 Nominal Strain at Break, 50 mm/min (Dry) 24 % ISO 527-1/-2 Nominal Strain at Break, 50 mm/min (Cond.) min. 50 % ISO 527-1/-2 Tensile Creep Modulus (1000 H, Strain < 0.5%, at 23°C) (Cond.) 700 MPa ISO 899-1 Flexural Modulus (Dry) 2800.0 MPa ISO 178 Charpy Unnotched Impact Strength (23°C) (Cond.) N kJ/m² ISO 179/1eU Charpy Unnotched Impact Strength (23°C) (Dry) N kJ/m² ISO 179/1eU Charpy Unnotched Impact Strength (at -30°C)(Dry) 100.0 kJ/m² ISO 179/1eU Izod Notched Impact Strength (23°C) (Dry) 5.5 kJ/m² ISO 180/A Charpy Notched Impact Strength (Dry) (at -30°C) 4 kJ/m² ISO 179/1eA Izod Notched Impact Strength (23°C) (Cond.) N kJ/m² ISO 180/A Izod Notched Impact Strength (Dry) (at 30°C) 5 kJ/m² ISO 180/A Charpy Notched Impact Strength (23°C) (Dry) 5.5 kJ/m² ISO 179/1eA Charpy Notched Impact Strength (-40°C) (Dry) 3 kJ/m² ISO 179/1eA Charpy Notched Impact Strength (23°C) (Cond.) 60 kJ/m² ISO 179/1eA Charpy Notched Impact Strength (-40°C) (Cond.) 3 kJ/m² ISO 179/1eA Deflection Temperature Under Load 1.8 Mpa (HDT B) 60.0 °C ISO 75-1/-2 Deflection Temperature Under Load 0.45 MPa (HDT B) 180.0 °C ISO 75-1/-2 Temperature Index at 50% Loss of Tensile Strength after 5000 H 112 °C IEC 60216 - Typical Properties
Value Units Test Method / Conditions Polymer Abbreviation (at 23°C) PA6 - - Density (at 23°C) 1130 kg/m³ ISO 1183 Viscosity Number (0.5% in 96% H₂SO₄) (at 23°C) 150 cm³/g ISO 307, 1157, 1628 Water Absorption (Equilibrium in Water, at 23°C) 9 - 10 % Similar to ISO 76 Moisture Absorption, Equilibrium (at 23°C/50% r.h) 2.6 - 3.4 % Similar to ISO 77 Melt Volume Rate (275°C/5 Kg at 23°C) 160 cm³/10min ISO 1133 Bulk Density 0.7 g/cm³ - - Thermal Properties
Value Units Test Method / Conditions Service Temperature max. 180 °C - Temperature Index (at 50% loss of tensile Strength after 20000 H) 100 °C IEC 60216 Coefficient of Linear Thermal Expansion, Longitudinal (at 23°C - 55°C) 102.0×10⁻⁶ /K ISO 11359-1/-2 Thermal Conductivity 0.33 W/(m K) DIN 52612-1 Specific Heat Capacity 1700 J/(kg*K) - - Electrical Properties
Value Units Test Method / Conditions Relative Permittivity (1 Mhz) (Dry) 3.5 - IEC 62631-2-1 Relative Permittivity (1 Mhz) (Cond.) 7 - IEC 62631-2-1 Dissipation Factor (1 Mhz) (Dry) 230.0×10⁻⁴ IEC 62631-2-1 Dissipation Factor (1 MHz) (Cond.) 3000.0×10⁻⁴ IEC 62631-2-1 Volume Resistivity (Cond.) 1×10⁹ Ohm.m IEC 62631-3-1 Volume Resistivity (Dry) 1×10¹² Ohm.m IEC 62631-3-1 Surface Resistivity (Cond.) 1×10⁹ Ohm IEC 62631-3-2 Surface Resistivity (Dry) 1×10¹² Ohm IEC 62631-3-2 Comparative Tracking Index - CTI 600 - IEC 60112,Test LIquid A - Shrinkage
Value Units Test Method / Conditions Molding Shrinkage (Normal) 0.75 % ISO 294-4 Processing Shrinkage, Constrained, Longitudinal (Tm = 260°C, Tw = 60°C) ⁴ 0.65 % - - Flammability
Value Units Test Method / Conditions Ul94 Flammability Rating (at Nominal 1.5mm) HB (1.5) class (mm) IEC 60695-11-10 Ul94 Flammability Rating V-2 (3.05) class (mm) IEC 60695-11-10 Yellow Card available Yes - - Automotive Materials (Thickness > 1mm) ⁴ Passed - ISO 3795, FMVSS 302 - Injection Molding
Value Units Test Method / Conditions Melt Temperature (Range) 250 - 270 °C Mold Temperature (Range) 40 - 60 °C - Residence Time max. 10 min - - Drying
Value Units Test Method / Conditions Moisture Content (Recommended) ¹ 0.03 - 0.06 % - Dryer Temperature ² 80 °C - Drying Time ³ 4 h - - Machine Settings
Value Units Test Method / Conditions Temperature Hopper Throat 80 °C - Cylinder Temperature 1 (Feed Zone) 240 °C - Cylinder Temperature 2 (Compression) 250 °C - Cylinder Temperature 3 (Metering - Zone, in Front of The Screw) 260 °C - Cylinder Temperature 4 (Nozzle) 260 °C - Peripheral Screw Speed max. 0.6 m/s - - Processing Properties
Value Units Test Method / Conditions Melting Temperature 220 °C ISO 11357-1/-3 /DSC Melt Volume-Flow Rate (275°C/5 Kg) 160.0 cm³/10min ISO 1133 Melt Temperature (Injection Molding/Extrusion) 250 - 270 °C - Mold Temperature (Injection Molding) 40 - 60 °C - Molding Shrinkage, Constrained ³ 0.65 % - Molding Shrinkage (Normal) 0.75 % ISO 294-4 - Note
- If product name or properties don't state otherwise.
- The asterisk symbol '*' signifies inapplicable properties.
- Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 260°C, TW = 60°C
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
Safety & Health
- Product Safety
In case processing is done under conditions as recommended (cf. processing data sheet) melts are thermally stable and do not generate hazards by molecular degradation or the evolution of gases and vapors.
Like all thermoplastic polymers the product decomposes on exposure to excessive thermal load, e.g. when it is overheated or as a result of cleaning by burning off.
Packaging & Availability
- Packaging Information
Standard packs are bag and bulk container (octagonal IBC=intermediate bulk container made from corrugated board with a liner bag).
Other packaging materials and shipping in road or rail silo wagons are possible by agreement.
Storage & Handling
- Storage Information
The containers should only be opened immediately before processing or drying.
To ensure that the delivered product absorbs as little moisture as possible, the containers should be stored in dry rooms and always carefully closed again after partial quantities have been withdrawn.
In principle, the product can be stored for a long period of time.
Containers stored in cold rooms should be equalized to ambient temperature before opening in order to avoid condensation on the granules.
Regardless of the storage conditions, the product should be pre-dried according to our recommendations and the machine should preferably be loaded using a closed conveyor system.