- Color (Properties)
- Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength (at 23°C) 50.0 kJ/m² ISO 179/1eU Charpy Notched Impact Strength (at 23°C) 8.0 kJ/m² ISO 179/1eA Tensile Modulus 11500.0 MPa ISO 527-1/-2 - Typical Properties
Value Units Test Method / Conditions Water Absorption (Equilibrium in Water, at 23°C) 0.40 - 0.40 % similar to ISO 62 Moisture Absorption, Equilibrium (at 23°C/50% r.h) 0.20 - 0.20 % similar to ISO 62 Density 1680 kg/m³ ISO 1183 - Thermal Properties
Value Units Test Method / Conditions HDT B (0.45 MPa) 220 °C ISO 75-1/-2 HDT A (1.80 MPa) 195 °C ISO 75-1/-2 Melting Temperature (10°C/min) 223.0 °C ISO 11357-1/-3,DSC Coeff. of Linear Thermal Expansion (Normal at 23°C - 55°C) 28.00 - 28.00 x 10⁻⁶ /K ISO 11359-1/-2 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity 1×10¹⁴ Ohm.m IEC 62631-3-1 - Specifications
Value Units Test Method / Conditions Viscosity Number 108 cm³/g ISO 307, 1157, 1628 - Rheological Properties
Value Units Test Method / Conditions Melt Volume-Flow Rate 19 cm³/10min ISO 1133 Molding Shrinkage (Normal) 0.94 % ISO 294-4 Molding Shrinkage (Parallel) 0.28 % ISO 294-4