Properties
- Color (Properties)
- Mechanical Properties
Value Units Test Method / Conditions Yield Strain (50 mm/min) 3.7 % ISO 527-1/-2 Charpy Notched Impact Strength (at 23°C) 5 kJ/m² ISO 179/1eA Charpy Impact Strength (at -30°C) 180 kJ/m² ISO 179/1eU Yield Stress (50 mm/min) 55 MPa ISO 527-1/-2 Charpy Notched Impact Strength (at -30°C) 4 kJ/m² ISO 179/1eA Tensile Modulus 2500.0 MPa ISO 527-1/-2 - Typical Properties
Value Units Test Method / Conditions Water Absorption (Equilibrium in Water, at 23°C) 0.50 - 0.50 % similar to ISO 62 Moisture Absorption, Equilibrium (at 23°C/50% r.h) 0.25 - 0.25 % similar to ISO 62 Density 1300.0 kg/m³ ISO 1183 - Thermal Properties
Value Units Test Method / Conditions HDT B (0.45 MPa) 165 °C ISO 75-1/-2 HDT A (1.80 MPa) 65 °C ISO 75-1/-2 Melting Temperature (10°C/min) 223.0 °C ISO 11357-1/-3 Thickness Tested (b1) 0.75 mm IEC 60695-11-10 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity 1×10¹⁴ Ohm.m IEC 62631-3-1 - Specifications
Value Units Test Method / Conditions Viscosity Number 130 cm³/g ISO 307, 1157, 1628 - Rheological Properties
Value Units Test Method / Conditions Melt Volume-Flow Rate 21 cm³/10min ISO 1133 Molding Shrinkage (Normal) 1.9 % ISO 294-4 Molding Shrinkage (Parallel) 1.6 % ISO 294-4